Hydroxyapatite Coating on Stainless Steel ۳۱۶L using Flame Spray Technique
محل انتشار: ماهنامه بین المللی مهندسی، دوره: 34، شماره: 2
سال انتشار: 1400
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 183
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJE-34-2_022
تاریخ نمایه سازی: 6 اردیبهشت 1400
چکیده مقاله:
This study was a preliminary study on flame spray coating with hydroxyapatite (HAp). Coating is one of the technique to improve metal resistance to corrosion. In this study, flame spray coating using HAp was performed on stainless steel ۳۱۶ L as a material for medical devices. This synthetic compound contains elements which are biocompatible and bioactive in human body where they can stick to body tissues or muscles.HAp has been extensively used as a bone substitute because of its crystal structure, biocompatibility and osteoconductive nature. In this study, ۳۱۶L SS was coated by HAp using flame spray method with varied oxygen flowrate and air pressure. The result of this study showed that the air pressure of ۱ bar and oxygen flowrate of ۲۵ l/min had the thickest coating which was ۱۲۳.۵μm and the lowest corrosion rate which was ۰.۰۲۶۱ mm/year. The air pressureof ۳ bar and oxygen flowrate of ۳۵ l/min produced the lowest thickness which was ۳۲.۵μm and the highest corrosion rate which was ۰.۰۷۶۱ mm/year. The use of high air pressure and oxygen flowrate decreased the coating thickness and the corrosion rate. The result revealed that flame spray method was effective to be used to coat HAp on ۳۱۶L SS.
کلیدواژه ها:
نویسندگان
F. Gapsari
The Mechanical Engineering Department of Brawijaya University, Malang, Indonesia
N. Hidayatia
The Mechanical Engineering Department of Brawijaya University, Malang, Indonesia
P. Setyarini
The Mechanical Engineering Department of Brawijaya University, Malang, Indonesia
M Alan
The Mechanical Engineering Department of Brawijaya University, Malang, Indonesia
R. Subagyo
MechanicalEngineering Department, University of Lambung Mangkurat, Banjarmasin, Indonesia
A. Andoko
Mechanical Engineering Department, State University of Malang, Malang, Indonesia
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :